What are the benefits of using cast copper rotors in high efficiency motors?

Induction motor rotors were traditionally made by die casting aluminium around a stack of steel laminations, so forming the rotor bars and end rings. Copper has much better conductivity, which would result in better efficiency, but was not used because it was difficult to die-cast due to its higher melting point.  The casting issues have now been solved by improvements in die materials and process control.

Using copper offers a range of options to the motor designer.  If the rotor size is unchanged, efficiency can be improved. On the other hand, the rotor size can be reduced while maintaining the original efficiency, so reducing the cost.

I am using CW614N (CZ121) to make machined components for a major motor manufacturer. The process results in about 3 tonnes per week of brass swarf which is contaminated with machining oil. Could this still be recycled?

Yes, brass swarf is very valuable and should be recycled. The brass industry relies on recycling for its survival; they will be able to clean the oil from the swarf before remelting it.

I understand that welding may have an effect on the corrosion resistance of the nickel aluminium bronzes. If so what treatment may be carried out to reduce this effect?

Yes, the heating effect of welding has the effect of producing a phase change in the alloy which on cooling leads to the formation of the corrodable martensitic beta phase. Annealing at 675oC for 2 to 6 hours after welding restores the pre weld structure and relieves stress. It is very effective in resisting subsequent corrosion.

Javítható a CW307G (CuAl10Ni5Fe4) alumínium bronz korrózióállósága hőkezeléssel?

Igen, ennek módja megtalálható a 02-833 Def Stan szabványban. Az extrudált rudak és profilok esetén 40 mm méret alatt a lágyítást 740°C plusz-mínusz 20°C hőmérsékleten végezzük, ezt követi a levegőhűtés. Ez a kötelező hőkezelés megszünteti azon fázisokat, melyek szelektív korrózióhoz vezethetnek a tengeri környezetben.

Mi a rézcsövek alumínium bordákkal történő alkalmazásának történelme?

A rézcsöves, alumínium bordás kondenzátor a légkondicionáló berendezések győztes kombinációja hosszú évek óta. A gyártók élvezik az egyszerű szerelhetőség előnyeit, míg a kivitelezők a rézcsövek egyszerű helyszíni szerelhetőségét és karbantarthatóságát emelnék ki. Még fontosabb talán, hogy ez a jól bejáratott technológia bizonyítottan tartós, hosszú élettartamú, az ügyelek legnagyobb megelégedésére.

What finishes are available for copper?

Bright copper, pre-oxidised copper, pre-patinated copper or post-patinated copper.

When flux has been used in jointing copper pipework do you have to flush the pipework afterwards?

Yes, any flux left inside the pipework must be removed after jointing is complete.

Javítható a CW307G (CuAl10Ni5Fe4) alumínium bronz korrózióállósága hőkezeléssel?

Igen, ennek módja megtalálható a 02-833 Def Stan szabványban. Az extrudált rudak és profilok esetén 40 mm méret alatt a lágyítást 740°C plusz-mínusz 20°C hőmérsékleten végezzük, ezt követi a levegőhűtés. Ez a kötelező hőkezelés megszünteti azon fázisokat, melyek szelektív korrózióhoz vezethetnek a tengeri környezetben.

What are the dimensional changes which take place on heat treating the age-hardenable copper alloys? What allowances should I make?

CuCr – this alloy is solution treated at 1000oC quenched and aged at about 470oC . The shrinkage on ageing is about 0.1 to 0.3%. However, the alloy is supplied fully heat treated (hard) so no further dimensional change will take place.

CuBe – this alloy is supplied solution treated (soft). It is machined first, then aged so the resultant shrinkage (0.1 to 0.3%) must be allowed for in design.

I have a number of machined aluminium bronze components which are to be packed in wooden boxes and shipped to Australia. How do I avoid corrosion/staining?

The key is to clean thoroughly, remove water, protect and keep dry:

1. After cleaning dry thoroughly using a de watering fluid such as WD40.
2. Remove displaced water with forced warm air.
3. Coat with protective coating such as benzotriazole inhibitor or a block copolymer.
4. Pack into benzotriazole treated paper lined wooden boxes. Moisture absorbent granules may also be used to keep the air inside the boxes dry.
5.Remove the coatings with a phosphoric based solution.
6. Dry thoroughly.

When flux has been used in jointing copper pipework do you have to flush the pipework afterwards?

Yes, any flux left inside the pipework must be removed after jointing is complete.

Je bezpečná měď, když inaktivuje mikroby?

Ano. Měděné, mosazové a bronzové povrchy jsou bezpečné, s dlouhou životností. Měď je stopovým prvkem pro lidský organismus spolu se zinkem a železem. Dospělí potřebují denní dávku 1mg pro uchování svého zdraví. Denní příjem mezi 1 a 11mg je pro organismus bezpečný. Potravinami obsahujícími ve větším množství měď jsou čokoláda, ořechy a semena. Vyrovnaná strava nám zabezpečuje dostatečný příjem mědi, takže se nedostatku mědi nemusíme obávat.